You are here: Home » Products » Super Hard 2000 Series 2024 10mm Anodized Aluminum Hex Bar Rod for Truck Wheel
Super Hard 2000 Series 2024 10mm Anodized Aluminum Hex Bar Rod for Truck Wheel
Click image to view full size image
|
|
Product: |
Views:101Super Hard 2000 Series 2024 10mm Anodized Aluminum Hex Bar Rod for Truck Wheel |
Unit price: |
Negotiable |
MOQ: |
|
Quantity: |
|
Delivery date: |
Since the payment date Days delivery |
Valid until: |
Long-term effective |
Last updated: |
2017-09-07 14:47 |
|
|
|
Item |
2024 10mm Anodized Aluminum Hex Bar Rod |
Grade |
1060,1100,1200,2024,2124,2014,2124,3003,3006,3030,5052, 5083,5154,5454,5754,5005,5652,6061,6062,6063,7075,etc |
Standard |
GB/T3191-1998,ASTM B221M-05A,JIS H4040-2006,etc |
Diameter |
2-250mm |
Length |
2m,3m,5.8m,6m,or as required |
Finish Condition |
O,H14,H12,H16,H18,H22,H112,T5,T6,T651,T351,T42,T451,T62,T3,T81,etc |
Surface |
Mill finish, polished, anodizing, ,powder coating, etc |
Package |
Standard export package ,or as required |
Application |
2024 aluminum hex bar rods are high strength hard aluminum, can be heat treatment to strengthen, in the quenching and quenching state of plastic medium, spot welding is good, with gas welding when the tendency to form intergranular cracks, the alloy in the quenching and cold hardening after its Cutting performance is good, after annealing can be low machinability: corrosion resistance is not high, often using anodizing and coating method or surface coated with aluminum layer to improve its corrosion resistance. Mainly used to make a variety of high-load parts and components (but not including stamping parts forging) such as aircraft on the skeleton parts, skin, frame, ribs, spars, rivets and other working parts below 150℃. |
Chemical Composition |
Grade |
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Ni |
Zn |
Ti |
Zr |
Al |
2024 |
0.5 |
0.5 |
3.8-4.9 |
0.3-0.9 |
1.2-1.8 |
0.1 |
— |
0.25 |
0.15 |
— |
Balance |
Mechanical Properties |
Grade |
Temper |
Thickness(mm) |
Tensile Strength(Mpa) |
Yield strength(Mpa) |
Elongation(%) |
2024 |
T4 |
5-85 |
≥500 |
≥315 |
≥10 |
|